6082-T6151 aluminum alloy is a heat-treated state of 6082 aluminum, where the state "T6151" refers to a specific heat treatment process that gives the alloy certain mechanical properties.
6082 aluminum alloy belongs to the aluminum-magnesium-silicon system, which is a high-strength alloy with good corrosion resistance, formability, and weldability. It is widely used in construction, transportation, mechanical structures, and other fields. Its strength and durability make it the first choice for applications requiring high-strength materials.
6082-T6151 aluminum alloy, with its high strength and excellent corrosion resistance, makes it suitable for a variety of applications requiring high strength and durability. In construction, transportation, mechanical structures, and aerospace, the application of 6082-T6151 aluminum alloy ensures better durability and safety for the components in these fields.
| Application Field | Description |
| Building Structures | 6082-T6151 aluminum alloy, with its excellent strength and corrosion resistance, is widely used in building frames, support structures, beams, and other elements. Its high strength provides stable support for construction projects that require high load-bearing capacity, especially in environments requiring durability and corrosion resistance, such as marine climates or humid regions. Moreover, the good workability of 6082-T6151 aluminum alloy makes it easier to shape and assemble during construction, improving the overall structural safety and service life of buildings. |
| Transportation | 6082-T6151 aluminum alloy is widely used in the manufacturing of automotive, ship, and railway vehicle components in the transportation industry. Due to its excellent strength and corrosion resistance, it is suitable for parts that need to withstand heavy loads and environmental exposure. For example, in automotive manufacturing, 6082-T6151 aluminum alloy provides strong support while reducing the vehicle's weight and improving fuel efficiency. In ships and railway vehicles, it not only enhances the reliability of the structure but also effectively resists corrosion from seawater and moisture, extending the service life of the components. |
| Mechanical Structures | 6082-T6151 aluminum alloy is used in heavy-duty mechanical structures, especially in applications such as cranes, bridges, and wind turbine towers. The high strength and outstanding corrosion resistance of this alloy make it reliable for use in mechanical structures that require load-bearing capacity and stability. Large facilities like wind turbine towers have extremely high demands on material strength and durability, and 6082-T6151 aluminum alloy meets these requirements, ensuring long-term stable operation of these structures in harsh environments. |
| Aerospace | In the aerospace industry, 6082-T6151 aluminum alloy is used in the manufacture of light aircraft and aircraft components. Its high strength, low density, and excellent corrosion resistance make it an ideal aerospace material. Through solution heat treatment and artificial aging, 6082-T6151 aluminum alloy provides excellent strength and toughness, ensuring the safety and stability of aircraft structures. Additionally, its good machinability and weldability make it advantageous in the production of complex aerospace components, and it is widely used in key parts such as fuselage frames, cabins, and wings. |
| Property | 6082-T651 Aluminum |
| Brinell Hardness | 91 |
| Elastic (Young's) Modulus, GPa | 69 |
| Elongation at Break, % | 6.3 |
| Fatigue Strength, MPa | 94 |
| Poisson's Ratio | 0.33 |
| Shear Modulus, GPa | 26 |
| Shear Strength, MPa | 190 |
| Tensile Strength: Ultimate (UTS), MPa | 320 |
| Tensile Strength: Yield (Proof), MPa | 270 |
| Property | 6082-T651 Aluminum |
| Latent Heat of Fusion, J/g | 410 |
| Maximum Temperature: Mechanical, °C | 170 |
| Melting Completion (Liquidus), °C | 650 |
| Melting Onset (Solidus), °C | 580 |
| Specific Heat Capacity, J/kg-K | 900 |
| Thermal Conductivity, W/m-K | 160 |
| Thermal Expansion, µm/m-K | 23 |
| Property | 6082-T651 Aluminum |
| Electrical Conductivity: Equal Volume, % IACS | 42 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 140 |