6082 O aluminum alloy plate has relatively low strength but excellent ductility and machinability, making it particularly suitable for components that require complex shapes and fine machining. It also offers good corrosion resistance and fatigue resistance, making it widely used in various industrial fields.
6082 O Aluminum Plate is an aluminum alloy sheet that offers good ductility, machinability, and corrosion resistance. It is primarily used for structural components and manufacturing processes with low to medium strength requirements.
6082 aluminum alloy is a commonly used medium-strength aluminum alloy, widely applied in engineering and manufacturing fields, especially in applications that require high corrosion resistance and good machinability.
| Characteristics/Factor | Description |
| Ductility | 6082 O aluminum plate has very high ductility, making it highly suitable for forming, bending, stamping, and stretching operations. It is particularly effective in producing parts with complex shapes. The high ductility helps prevent cracking during deep drawing processes. |
| Strength | Although 6082 aluminum plate in the O state has lower strength compared to other heat-treated aluminum alloys (such as T6 or T4), it still meets the requirements for low to medium strength applications and is suitable for components or parts that do not bear extreme loads. |
| Corrosion Resistance | 6082 aluminum alloy has good corrosion resistance, making it suitable for use in humid or harsh environments. It has strong resistance to most corrosive media, making it an ideal material for marine, transportation, and other applications involving water or moisture. |
| Weldability | 6082 O aluminum plate has excellent weldability and can be processed using various welding techniques, including TIG (Tungsten Inert Gas) and MIG (Metal Inert Gas) welding. This makes it an ideal choice for welding components together. |
| Fatigue Resistance | This alloy exhibits good fatigue resistance, making it suitable for applications subjected to repeated loads. It is particularly ideal for components that require long-term use and are subjected to repeated stretching, bending, or vibration, such as transportation vehicles and mechanical structures. |
| Machinability | 6082 O aluminum plate has excellent machinability and is suitable for various machining operations, including cutting, drilling, bending, and stamping. Its good machinability makes it easy to manufacture complex shapes and precision parts without affecting the final part quality. |
| Heat Treatment | In the O state, 6082 aluminum alloy has high ductility. If increased strength and hardness are required, it can typically be converted to the T6 state through a heat treatment process, which significantly enhances its strength and makes it more suitable for high-load applications. |
| Alloy | 6082 |
| Temper | O, T4 |
| ABS sheet dimension: | Thickness: 0.30-3.50mm |
| Width: 52-2400mm | |
| Length: 500-10000mm | |
| ABS coil dimension: | Thickness: 0.30-3.50mm |
| Width: 52-2400mm | |
| Standard | GB/T 33227-2016, JIS H4000, ASTM B209, EN 485 |
| Element | Composition (%) |
| Si | 0.7-1.30 |
| Fe | 0.50 |
| Cu | 0.10 |
| Mn | 0.40-1.0 |
| Mg | 0.60-1.20 |
| Cr | 0.25 |
| Ni | - |
| Zn | 0.20 |
| Ti | 0.10 |
| Al | Remainder |
| Property | 6082-O Aluminum |
| Brinell Hardness | 40 |
| Elastic (Young's, Tensile) Modulus, GPa | 69 |
| Elongation at Break, % | 18 |
| Fatigue Strength, MPa | 91 |
| Poisson's Ratio | 0.33 |
| Shear Modulus, GPa | 26 |
| Shear Strength, MPa | 84 |
| Tensile Strength: Ultimate (UTS), MPa | 140 |
| Tensile Strength: Yield (Proof), MPa | 85 |
| Property | 6082-O Aluminum |
| Latent Heat of Fusion, J/g | 410 |
| Maximum Temperature: Mechanical, °C | 170 |
| Melting Completion (Liquidus), °C | 650 |
| Melting Onset (Solidus), °C | 580 |
| Specific Heat Capacity, J/kg-K | 900 |
| Thermal Conductivity, W/m-K | 160 |
| Thermal Expansion, µm/m-K | 23 |
| Property | 6082-O Aluminum |
| Electrical Conductivity: Equal Volume, % IACS | 42 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 140 |
6082 O aluminum plate finds wide-ranging applications in industries requiring a combination of strength, corrosion resistance, and formability.
Which aluminum is stronger 6061 or 6082?
Strength comparison: 6061 aluminum is typically stronger than 6082 aluminum.
What is aluminum 6082 used for?
Uses of 6082 aluminum: Aluminum 6082 is commonly used in structural applications such as bridges, cranes, and trusses due to its good mechanical properties and weldability.
What is the difference between Aluminium 6082 T6 and 6082?
Aluminum 6082 is the alloy, whereas 6082 T6 is a temper designation indicating the material has been solution heat-treated and artificially aged to achieve a certain level of hardness and strength.